GeKa Elıf Lux Bff Tozaltı Kaynak Tozu
Normları
|
TS EN ISO 14174 |
SA FB 1 65 DC H5 |
|
EN ISO 14174 |
SA FB 1 65 DC H5 |
|
AWS A5.17 |
F7A4-EM12/F7A4-EM12K/ F7A4-EH12K |
|
AWS A5.23 |
F8A4-EA2-A2/ F9A4-EF3(mod)-F3 / F11A8-EM4(mod)-M4 |
Kaynak Metalinin Kimyasal Analizi % (Tipik)
|
Tozaltı Kaynak Teli |
C |
Si |
Mn |
Mo |
Ni |
Cr |
|
S2 |
0.05 |
0.20 |
1.00 |
--- |
--- |
--- |
|
S2 Si |
0.06 |
0.30 |
1.10 |
--- |
--- |
--- |
|
S2 Mo |
0.07 |
0.25 |
1.15 |
0.45 |
--- |
--- |
|
S3 Si |
0.10 |
0.60 |
1.70 |
--- |
--- |
--- |
|
S3 NiMo 1 |
0.09 |
0.25 |
1.65 |
0.55 |
0.90 |
--- |
|
S3 NiCrMo 2.5 |
0.06 |
0.30 |
1.50 |
0.50 |
2.20 |
0.50 |
Mekanik Özellikler
|
Tozaltı Kaynak Teli |
AWS A5.17 / AWS A5.23 |
Akma Dayanımı (N/mm²) |
Çekme Dayanımı (N/mm²) |
Uzama (Lo=5do) (%) |
Çentik Darbe Dayanımı (ISO-V/-20°C) (Joule) |
Çentik Darbe Dayanımı (ISO-V/-30°C) |
Çentik Darbe Dayanımı (ISO-V/-40°C) |
Çentik Darbe Dayanımı (ISO-V/-60°C) |
|
S2 |
F7A4-EM12 |
410 |
520 |
24 |
--- |
70 J |
60 J |
--- |
|
S2 Si |
F7A4-EM12K |
450 |
540 |
23 |
--- |
--- |
65 J |
--- |
|
S2 Mo |
F7A4-EH12K |
480 |
570 |
27 |
--- |
--- |
70 J |
--- |
|
S3 Si |
F8A4-EA2-A2 |
490 |
580 |
26 |
--- |
--- |
60 J |
--- |
|
S3 NiMo1 |
F11A8-EM4(mod)-M4 |
580 |
650 |
21 |
100 J |
--- |
60 J |
--- |
|
S3NiCrMo2.5 |
F9A4-EF3(mod)-F3 |
740 |
850 |
20 |
90 J |
--- |
85 J |
min.27 J |
Kullanıldığı Yerler ve Özellikleri
Florid-bazik aglomere tip kaynak tozudur
Düşük alaşımlı yüksek mukavemetli çeliklerin kaynağı için uygundur
Daha yüksek manganez içeren tozaltı tellerinin kombinasyonlarında tercih edilir.
Yüksek tokluk gerektiren çok pasolu kaynak uygulamalarına yatkındır
Toz kullanılmadan önce 300°C - 350°C’de 2 saat kurutulmalıdır.
Bazisite
|
Bazisite |
3.0 |
Ambalaj Bilgileri ve Parametreler
|
Ürün Kodu |
Paketleme Tipi |
Ağırlık (Kg) |
|
3010800061 |
Kraft Torba |
25 |
Onaylar
with GeKa S3Si
ABS
ABS
ABS
ABS DNV-GL
BV BV BV DB UKR SEPRO